  • Name: Silver Color PU Reflective Transfer Film for Strechable Fabric
  • Number: 4001-P
  • Standard: EN ISO 20471:2013 ANSI/ISEA 107:2010 AS/NZS 1906 OKEO-TEX 100 CAS-Z96-02
  • Reflection: >500cd/(lx ㎡)
  • Washing: Domestic Wash≥50 cycles@60°C (ISO 6330)
  • Backing: BPU
  • Color available: Silver
  • Specification: 2.5cm*100M/Roll, 5.0cm*100m/Roll, other size upon request.
  • Application: Ideal for High Visibility Work Wear, Protective Uniforms, Sportswear, School Uniforms ,Fashion Wear

HIGHVIZ 4001-P Silver PU Reflective Transfer Film, composed of micro glass beads bonded to heat activated adhesive, with a transparent plastic cover to protect the reflective side during application and an extra plastic liner to protect the adhesive side.

 

HIGHVIZ 4001-P Silver can be heat applied to occupational apparel, work wear, sports wear, school uniforms, especially elastic and stretchable substrates . It can also can be laser cutting into graphics, characters and LOGOs as per customers' requirements.

 

HIGHVIZ 4001-P Elastic Reflective Transfer Film makes people visible in darkness, fog and raining weather to decrease dangers, also work as an element in the fashion industry.

 

Physical Performance:

 

 Certificate: EN ISO 20471:2013 ANSI/ISEA 107:2010 AS/NZS 1906 OKEO-TEX 100 CAS-Z96-02

     Backing: BPU

     Color Available: Silver

     Retro-reflection: >500cd/(lx ㎡)

     Wash: Domestic Wash≥50 cycles@60°C (ISO 6330)

     Dry Clean: ≥50circles (ISO 3175)

     Spec: 2.5cm*100M/Roll, 5.0cm*100m/Roll, other size upon request.

     Application: Ideal for High Visibility Work Wear, Protective Uniforms, Sportswear, School Uniforms ,Fashion Wear, Fashion Bags and so on.

 

Retro-reflection Performance:

Initial coefficient of retro-reflection performance in cd/(lx ㎡)

                

              4001-P: Silver Elastic Reflective Transfer film, BPU Backing

 

Observation

Angle

          Entrance     Angle

       5°

      20°

      30°

      40°

Test

Certificate

Test

Certificate

Test

Certificate

Test

Certificate

    0.2°

 523

≥330

 537

≥290

 476

≥180

 274

≥65

   0.33°

 355

≥250

 359

≥200

 340

≥170

 230

≥60

    1°

  37

≥25

 42

≥15

 46

≥12

  31

≥10

   1°30′

  20

≥10

 20

≥7

 20

≥5

 21

≥4

 

Test Result of 4001-P Silver Elastic Reflective Transfer film

  1.1 Abrasion

The test sample shall be abraded in accordance with EN 530:1994, method 2, using the woolen fabric abradant. The specimens shall be measured after 5 000 cycles and at a pressure of 9 KPa.

 Retro-reflection after Abrasion

 

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

  Result

 5°

   0.2°

   449

    100

   PASS

 

1.2 Flexing

The test sample shall be flexed in accordance with EN ISO 7854:1997 method A. The specimens shall be measured after 7 500 cycles.

 Retro-reflection after Flexing

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

  Result

  0.2°

    446

    100

   PASS

 

1.3 Folding at cold temperatures

The test sample shall be exposed and folded in accordance with ISO 4675 at a temperature of (-20 ± 1)°C.

Measurements shall be made after reconditioning to the atmosphere for at least 2 h.

 Retro-reflection after Folding at cold temperatures

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

  Result

   5°

    0.2°

   466

    100

   PASS

 

1.4 Exposure to temperature variation

Specimens of the size of 180 mm x 30 mm shall be exposed continuously to a cycle of changing temperatures:

a) for 12 h at (50 ± 2) °C immediately followed by

b) 20 h at (-30 ± 2) °C

c) Conditioning for at least 2 h in accordance with 7.1.

Retro-reflection after Temperature Variation

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

  Result

   0.2°

   479

    100

   PASS

 

1.5 Wash, Dry Clean

  After 25 wash, washing procedure in accordance with ISO 6330:2000+A1:2009, method 2A, dried at (50 ± 5) °C.

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

   Result

  5°

   0.2°

    363

    100

   PASS

 

After 50 wash, washing procedure in accordance with ISO 6330:2000+A1:2009, method 2A, dried at (50 ± 5) °C.

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

   Result

  5°

   0.2°

    291

    100

   PASS

After 50 cycles washing, no Breakage, detachment, discoloration

After 5 cycles dry washing, no Breakage, detachment, discoloration

 

1.6 Retro-reflective performance in rainfall

Samples shall be tested in accordance with Annex D of this standard. Exposure at 284mm/h water flow for 2 hours. Retro-reflection after rainfall

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

  Result

 12’

    257

    100

   PASS

 


The above test data is from SGS and SATRA laboratory test of HIGHVIZ received samples, final production will have ±3-5% tolerance, which is acceptable. 

no such related products!

CONTACT US

 

    HIGHVIZ INDUSTRIAL CO.,LTD.
  • Tel: 0086-579-89107556/89104099        
  • Cel &WhatsApp:  0086-15258945615           
  • Email: market@highviz-china.com
  • Website:  www.highviz-china.com
                                Copyright © HIGHVIZ INDUSTRIAL CO.LTD,   浙ICP备17014405号   Powered by:300.cn  Admin