  • Name: Silver Reflective Transfer Film for Plotter Cutting Graphics
  • Number: 4001-K
  • Standard: EN ISO 20471:2013 ANSI/ISEA 107:2010 AS/NZS 1906 OKEO-TEX 100
  • Reflection: >500cd/(lx ㎡)
  • Washing: Domestic Wash≥50 cycles@60°C (ISO 6330)
  • Backing: PES
  • Color available: Silver
  • Specification: 2.5cm*100M/Roll, 5.0cm*100m/Roll, other size upon request.
  • Application: Ideal for High Visibility Work Wear, Protective Uniforms, Sportswear, School Uniforms ,Fashion Wear

HIGHVIZ 4001-K Silver Reflective Transfer Film, composed of micro glass beads bonded to heat activated adhesive, with a transparent PET cover to protect the reflective side during application.

HIGHVIZ 4001-K Reflective Transfer Film can be plotter cutting or laser cutting into graphics, characters and LOGOs as per customers' requirements, then heat applied to occupational apparel, work wear, sports wear, school uniforms as well as different substrates to meet various fashion requirements.

 

HIGHVIZ 4001-K Reflective Transfer Film makes people visible in darkness, fog and raining weather to decrease dangers, also work as an element in the fashion industry.

 

Physical Performance:

     Certificate: EN ISO 20471:2013 ANSI/ISEA 107:2010 AS/NZS 1906 OKEO-TEX 100

     Backing: PES

     Color Available: Silver

     Retro-reflection: >500cd/(lx ㎡)

     Wash: Domestic Wash≥50 cycles@60°C (ISO 6330)

     Dry Clean: ≥50circles (ISO 3175)

     Spec: 2.5cm*100M/Roll, 5.0cm*100m/Roll, other size upon request.

 

     Application: Ideal for High Visibility Work Wear, Protective Uniforms, Sportswear, School Uniforms ,Fashion Wear, Fashion Bags and so on.

 

Retro-reflection Performance:

Initial coefficient of retro-reflection performance in cd/(lx ㎡)

                

              4001-K: Silver Reflective Transfer filmPES Backing

 

Observation

Angle

          Entrance     Angle

       5°

      20°

      30°

      40°

Test

Certificate

Test

Certificate

Test

Certificate

Test

Certificate

    0.2°

 523

≥330

 537

≥290

 476

≥180

 274

≥65

   0.33°

 355

≥250

 359

≥200

 340

≥170

 230

≥60

    1°

  37

≥25

 42

≥15

 46

≥12

  31

≥10

   1°30′

  20

≥10

 20

≥7

 20

≥5

 21

≥4

 

Test Result of 4001 Silver Reflective Transfer film

  1.1 Abrasion

The test sample shall be abraded in accordance with EN 530:1994, method 2, using the woolen fabric abradant. The specimens shall be measured after 5 000 cycles and at a pressure of 9 KPa.

 Retro-reflection after Abrasion

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

  Result

 5°

   0.2°

   449

    100

   PASS

 

1.2 Flexing

The test sample shall be flexed in accordance with EN ISO 7854:1997 method A. The specimens shall be measured after 7 500 cycles.

 Retro-reflection after Flexing

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

  Result

  0.2°

    446

    100

   PASS

 

1.3 Folding at cold temperatures

The test sample shall be exposed and folded in accordance with ISO 4675 at a temperature of (-20 ± 1)°C.

Measurements shall be made after reconditioning to the atmosphere for at least 2 h.

 Retro-reflection after Folding at cold temperatures

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

  Result

   5°

    0.2°

   466

    100

   PASS

 

1.4 Exposure to temperature variation

Specimens of the size of 180 mm x 30 mm shall be exposed continuously to a cycle of changing temperatures:

a) for 12 h at (50 ± 2) °C immediately followed by

b) 20 h at (-30 ± 2) °C

c) Conditioning for at least 2 h in accordance with 7.1.

Retro-reflection after Temperature Variation

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

  Result

   0.2°

   479

    100

   PASS

 

1.5 Wash, Dry Clean

  After 25 wash, washing procedure in accordance with ISO 6330:2000+A1:2009, method 2A, dried at (50 ± 5) °C.

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

   Result

  5°

   0.2°

    363

    100

   PASS

 

After 50 wash, washing procedure in accordance with ISO 6330:2000+A1:2009, method 2A, dried at (50 ± 5) °C.

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

   Result

  5°

   0.2°

    291

    100

   PASS

After 50 cycles washing, no Breakage, detachment, discoloration

After 5 cycles dry washing, no Breakage, detachment, discoloration

 

1.6 Retro-reflective performance in rainfall

Samples shall be tested in accordance with Annex D of this standard. Exposure at 284mm/h water flow for 2 hours. Retro-reflection after rainfall

Entrance  Angle

Observation Angle

Measured value (cd/(lx ㎡))

Minimum requirements (cd/(lx ㎡))

  Result

 12’

    257

    100

   PASS


 

 

The above test data is from SGS and SATRA laboratory test of HIGHVIZ received samples, final production will have ±3-5% tolerance, which is acceptable. 

no such related products!

CONTACT US

 

    HIGHVIZ INDUSTRIAL CO.,LTD.
  • Tel: 0086-579-89107556/89104099        
  • Cel &WhatsApp:  0086-15258945615           
  • Email: market@highviz-china.com
  • Website:  www.highviz-china.com
                                Copyright © HIGHVIZ INDUSTRIAL CO.LTD,   浙ICP备17014405号   Powered by:300.cn  Admin